摘要
The isothermal oxidation behavior of Fe-10 Al,Fe-15 Al,Fe-20 Al alloys with and without the addition of0.1 at% Y was studied at 800℃ under 1×105 Pa of flowing pure O2 for 24 h.The oxidation of three Fe-Al alloys can be divided into transient state and steady state oxidation stages.The oxidation of each stage is approximately in accordance with the parabolic law.The addition of 0.1 at% Y changes the oxidation behavior obviously and leads to a significant increase of the weight gain of Fe-10 Al and Fe-15 Al.The scale grown on Fe-10 Al is much thicker and more complicated than that grown on Fe-20 Al,which is composed of an exclusive thin layer of Al2 O3 protective film.Due to the formation of a large number of nodules,the scales grown on Fe-15 AI cannot provide full protection for the alloy.Scale micro structure of the three Fe-Al-0.1 Y alloys is similar to their corresponding Fe-Al alloys.However,nodules with very small size still appear on the surface of Fe-20 Al-0.1 Y alloy.The critical Al concentration to form an exclusive Al2 O3 protective layer for Fe-Al binary alloy is on the borderline between 15 at%-20 at%.For Fe-Al-0.1 Y alloy,the presence of 20 at% Al is not enough to inhibit the growth of nodules.
基金
Project supported by the National Natural Science Foundation of China (51701054)
the Science and Technology Research Program of Jiangxi Provincial Education Department of China (GJJ160770)。