摘要
在近共晶成分Al-Si-Mg合金中,加人锶(Sr)作为变质剂,研究变质时间对合金组织与性能的影响。结果表明,Sr能使共晶硅在铸态时呈团絮状,热处理后颗粒状的组织更细小。但是,随变质时间的延长,镁(Mg)、Sr含量会逐渐烧损,导致强化效果与变质效果削减,力学性能也随之降低,当变质时间为1h时,合金的综合力学性能最好,此时,其抗拉强度为325.6MPa,伸长率为8.3%。
In the near-eutectic Al-Si-Mg alloy,Strontian(Sr)was added as a modifier.The effect of Sr modification time on the microstructure and mechanical properties of the alloys were studied.The results show that Sr can make the eutectic silicon become flocculent in the as-cast state,and the particle microstructure became finer after heat treatment.However,with the increasing modification time,the content of Magnesium(Mg)and Sr was burning lost gradually,which caused the effect of strengthening and modification decreased,so did mechanical properties.The best comprehensive mechanical properties of the alloy were observed after being modified for an hour,which the tensile strength is 325.6 MPa and the elongation is 8.3%.
作者
李捷
张军
LI Jie;ZHANG Jun(State Grid Beijing Electric Power Company,Beijing 100031,China;China Electric Power Research Institute,Beijing 100055,China)
出处
《铸造技术》
CAS
2020年第10期913-915,929,共4页
Foundry Technology
关键词
Sr变质时间
近共晶Al-Si合金
电力金具材料
modification time of Sr
near eutectic Al-Si alloy
electric power fitting materials