摘要
以苯基三甲氧基硅烷为原料,在酸性条件下利用水解缩合法,制备得到了苯基多面体低聚倍半硅氧烷(苯基POSS)。将苯基POSS添加到硅树脂预聚体中,通过原位聚合法制备出苯基POSS/硅树脂复合材料。研究结果发现:当苯基POSS质量分数小于4.0%时,复合材料在可见光区的透光率均达到99.0%以上;当苯基POSS质量分数为4.0%时,复合涂层的折射率达到最大值1.54,硅树脂的初始热分解温度从256℃上升到370℃,复合涂层的附着力较佳,达到1级,同时苯基POSS对硅树脂复合材料的增韧效果明显。
Phenyl polyhedral oligomeric silsesquioxane(phenyl-POSS)was prepared by hydrolysis and condensation method under acid condition with phenyltrimethoxysilane as raw material.Phenyl-POSS/silicone resin composite was prepared by in-situ polymerization after adding phenyl-POSS to silicone resin prepolymer.The research results showed that when the mass fraction of phenyl-POSS was less than 4.0%,the light transmittance of the composite in the visible light region could reach above 99.0%.When the mass fraction of phenyl-POSS was 4.0%,the refractive index of the composite coating reached the maximum value of 1.54,and the initial thermal decomposition temperature of silicone resin was raised from 256℃ to 370℃,and the adhesion of the composite coating was excellent and reached grade 1.At the same time,the toughening effect of phenyl-POSS on silicone resin composite was obvious.
作者
董晓娜
付建平
游胜勇
谢欣
陈桂华
夏俊
Dong Xiaona;Fu Jianping;You Shengyong;Xie Xin;Chen Guihua;Xia Jun(Institute of Applied Chemistry,Jiangxi Academy of Sciences,Nanchang 330096,Jiangxi,China)
出处
《中国胶粘剂》
CAS
北大核心
2020年第10期20-23,共4页
China Adhesives
基金
江西省科技厅重点研发计划(20181BBE50005)。
关键词
苯基POSS
硅树脂
折射率
透光率
附着力
phenyl-POSS
silicone resin
refractive index
light transmittance
adhesion