Mg-3%Al alloy was refined by carbon inoculation combining with 0.2%Ca addition.High grain refining efficiency was obtained and the synergistic refining mechanism was deeply discussed in the present study.Al-C-O particles,actually Al4C3 particles,were formed in the carbon-inoculated Mg-3%A1 alloy acting as nuclei forα-Mg grains.Ca addition had no obvious effect on size distribution of the nucleating particles.Ca segregation was proved on Al4C3 particles,which should reduce the interfacial energy of nuclei/Mg.The constitutional undercooling in front of nucleus/liquid was increased from 0.12℃to 0.15℃induced by 0.2%Ca addition.The synergistic grain refining efficiency can be attributed to the higher constitutional undercooling and lower the interface energy of nucleus/Mg induced by Ca addition.More nucleating particles with small size could be activated acting as potent nuclei ofα-Mg grains.Consequently,Mg-3%Al alloy could be effectively refined due to the synergistic effect induced by carbon inoculation combining with Ca.
基金
This work was supported by the National Natural Science Foundation of China(51574127)
Natural Science Foundation of Guangdong Province(2014A030313221).