高碳硬线钢65Mn凝固末端电磁搅拌位置及连铸工艺优化 被引量:4

Optimization of electromagnetic stirring position at solidification end and continuous casting process of high carbon hard wire steel 65Mn
下载PDF
导出
摘要 近期生产的高碳硬线钢65Mn在拉拔过程中存在断丝现象,严重影响了生产节奏和产品质量。通过对近期生产的65Mn进行跟踪取样并对其铸坯(160 mm×160 mm)中心C偏析进行分析,发现铸坯中心的C偏析较为严重,分析认为末端电磁搅拌并未有效发挥减轻铸坯中心C偏析的作用,是导致65Mn钢凝固中心C偏析严重的主要原因。文中通过射钉实验,在保证末搅位置不变、满足连铸机大生产的情况下,分别在不同拉速和比水量条件下对末端电磁搅拌安装位置处65Mn的铸坯凝固壳厚度和液芯尺寸进行测定,对65Mn连铸工艺进行优化,并建立方坯凝固传热模型进行验证,有效减轻65Mn铸坯中心C偏析。 The wire breaking phenomenon of high carbon hard wire steel 65Mn produced recently has huge impact on productivity and product quality.The C segregation in the center of the slab(160 mm×160 mm)was analyzed by tracking and sampling 65Mn produced recently.It is considered that the end electromagnetic stirring does not play the most effective role in reducing the C segregation in the slab center,which is the main reason for serious C segregation in solidification center of 65Mn steel.In this paper,the thickness of solidified shell and the size of liquid core of 65Mn slab at the end electromagnetic stirring installation position were measured under different casting speed and specific water content by nail shooting experiment.The process of 65Mn continuous casting was optimized,and the solidification heat transfer model of billet was established for verification,which effectively reduced the central C segregation of 65Mn billet.
作者 张亚君 杨红来 张春斌 黄小山 张全庆 ZHANG Yajun;YANG Honglai;ZHANG Chunbin;HUANG Xiaoshan;ZHANG Quanqing(Xinyu Iron and Steel Group Co.,Ltd.,Xinyu 338001,Jiangxi,China)
出处 《江西冶金》 2021年第2期32-38,共7页 Jiangxi Metallurgy
关键词 65Mn 末端电磁搅拌 中心C偏析 工艺优化 65Mn end electromagnetic stirring central C segregation process optimization
  • 相关文献

参考文献8

二级参考文献57

共引文献44

同被引文献90

引证文献4

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部