摘要
采用气流磨分级技术对商业钨粉进行改性,研究气流磨处理和不同粒度搭配对钨粉粉末烧结体微观组织和力学性能的影响。结果表明,经气流磨分级处理后,粒度分布较窄的钨粉能实现良好的堆积均匀性,消除团聚体在烧结过程中形成的不规则粗孔,提升粉末烧结均匀性,提高烧结后期整体相对密度;烧结相对密度由90.7%提高至92.8%,抗弯强度由238.5 MPa提升至292.4 MPa。获得粒度分布窄、分散性好的钨粉可以消除烧结体中不规则粗孔,是提升烧结体力学性能的关键。
Commercial tungsten powders were modified by jet milling,the effects of jet milling treatment and particle size distribution on the microstructure and mechanical properties of the sintered tungsten body were studied.The results show that,the tungsten powders treated by jet milling in the narrower particle size distribution can achieve the better packing homogeneity,eliminate the irregular coarse pores formed during sintering,improve the sintering uniformity,and increase the relative density of the sintered body;the relative density of the sintered body increases from 90.7%to 92.8%,and the bending strength from 238.5 MPa to 292.4 MPa.The tungsten powders in the narrow particle size distribution with the good dispersibility can eliminate the irregular coarse pores in sintered body,which is the key factor to improve the mechanical properties of the sintered body.
作者
李星宇
章林
秦明礼
魏子晨
阙忠游
曲选辉
LI Xing-yu;ZHANG Lin;QIN Ming-li;WEI Zi-chen;QUE Zhong-you;QU Xuan-hui(Institute for Advanced Materials and Technology,University of Science and Technology Beijing,Beijing 100083,China)
出处
《粉末冶金技术》
CAS
CSCD
北大核心
2021年第3期251-257,共7页
Powder Metallurgy Technology
基金
国家重点研发计划专项资助项目(2017YFB0305600)
国家自然科学基金资助项目(51974029,52074032,52071013)
中央高校基本科研业务费(FRF-GF-20-27B,FRF-BD-20-23A)。
关键词
气流磨
钨粉
烧结
孔隙
微观组织
力学性能
jet milling
tungsten powders
sintering
pores
microstructure
mechanical properties