摘要
Antimony sulfide(Sb_(2)S_(3))is a promising anode for lithium-ion batteries due to its high capacity and vast reserves.However,the low electronic conductivity and severe volume change during cycling hinder its commercialization.Herein our work,a three-dimensional(3D)Sb_(2)S_(3) thin film anode was fabricated via a simple vapor transport deposition system by using natural stibnite as raw material and stainless steel fiber-foil(SSF)as 3D current collector,and a carbon nanotube interphase was introduced onto the film surface by a simple dropping-heating process to promote the electrochemical performances.This 3D structure can greatly improve the initial coulombic efficiency to a record of 86.6% and high reversible rate capacity of 760.8 mAh·g^(-1) at 10 C.With carbon nanotubes interphase modified,the Sb_(2)S_(3) anode cycled extremely stable with high capacity retention of 94.7% after 160 cycles.This work sheds light on the economical preparation and performance optimization of Sb_(2)S_(3)-based anodes.
基金
financially supported by the National Natural Science Foundation of China(No.51774343).