一种含锰铁精矿球团性能试验研究 被引量:5

Experimental study on pellets performance of a kind of manganese-containing iron concentrate
原文传递
导出
摘要 针对一种粒度较粗的含锰铁精矿用于生产球团时存在生球质量差和成品球强度低等问题,本文通过磨矿试验和造球实验,研究了含锰铁精矿粒度对膨润土配比的影响,并对最佳磨矿条件下的含锰铁精矿球团性能进行了系统研究。结果表明:含锰铁精矿的细度对于生球质量影响较小,对于降低膨润土配比的效果不明显,球团预热和焙烧所需温度均高于普通磁铁精矿;在球磨机细磨10 min,膨润土配比为2.0%的条件下可制备出合格生球;在预热温度为1 020℃,预热时间为20 min,焙烧温度为1 280℃,焙烧时间为25 min的条件下,成品球团抗压强度可以达到2 456 N/P,能够满足高炉生产要求。 Aiming at the problems of poor quality of green pellets and low strength of finished pellets when a kind of manganese-containing iron concentrate with coarse particle size is used, in this paper, through grinding and pelletizing experiments, the influence of the particle size of manganese-containing iron concentrate on the ratio of bentonite is studied, and the performance of manganese-containing iron concentrate pellets under optimal grinding conditions is systematically studied.The results show that the fineness of the manganese-containing iron concentrate has little effect on the quality of the green pellets, and the effect of reducing the ratio of bentonite is not obvious.The temperature required for pellet preheating and roasting is higher than that required for ordinary magnetite concentrate.The qualified green balls can be prepared under the condition of fine grinding in a ball mill for 10 min and a bentonite ratio of 2.0%.When the preheating temperature is 1 020 ℃,the preheating time is 20 min, the baking temperature is 1 280 ℃,and the baking time is 25 min, the compressive strength of the finished pellets can reach 2 456 N/P,which can meet the requirements of blast furnace production.
作者 滕飞 曾志彦 郭培民 TENG Fei;ZENG Zhiyan;GUO Peimin(State Key Laboratory of Advance Steel Process and Products,Central Iron and Steel Research Institute,Beijing 100081,China;China Minmetals Beryllium Co.,Ltd.,Hengyang 421513,Hunan,China)
出处 《烧结球团》 北大核心 2021年第5期47-53,共7页 Sintering and Pelletizing
关键词 铁精矿 尾矿资源 球团 磨矿 颗粒形貌 manganese iron concentrate tailings resource pellets ore grinding particle morphology
  • 相关文献

参考文献9

二级参考文献71

共引文献43

同被引文献50

引证文献5

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部