LB-10型冷补沥青混合料的制备及性能 被引量:1

Study on Preparation and Performance of LB-10 Cold Patch Asphalt Mixture
下载PDF
导出
摘要 为研究沥青冷补液各组分变化对冷补沥青混合料性能的影响,制备了冷补液组分设计不同的LB-10型冷补沥青混合料,研究了不同抗剥落剂掺量、沥青与柴油比例、冷补剂掺量对其施工和易性、马歇尔性能与水稳定性的影响规律.研究发现,随着抗剥落剂掺量的增加,混合料的贯入强度与马歇尔稳定度逐渐增大,柴油挥发率逐渐减小;而浸水残留稳定度呈先增加再减小的规律,在抗剥落剂掺量为0.36%时达到最高,为89.2%.随着沥青与柴油比例的增大,混合料贯入强度与浸水残留稳定度逐渐增大,且当沥青与柴油比例大于80∶14后,混合料马歇尔稳定度明显增强,高于7 kN,但施工和易性下降.随着冷补剂掺量的增加,混合料贯入强度逐渐增大,而柴油挥发率、马歇尔稳定度与浸水残留稳定度随掺量的增加呈先减小再增加的规律,在掺量为1.7%时浸水残留稳定度达到最高,为89.6%.综合考虑冷补沥青混合料的施工和易性,马歇尔性能及水稳定性,应控制冷补液中沥青与柴油比例为78∶20,冷补剂掺量为1.7%,抗剥落剂掺量为0.36%. In order to study the influence of components of bitumen cold rehydration fluid on the performance of cold patch asphalt mixture, LB-10 cold patch asphalt mixture with different composition designs of cold patch liquid was prepared, and the influence of different anti stripping agent content, asphalt to diesel ratio, and cold patch asphalt additive content on the construction workability, the Marshall performance and water stability of cold patched asphalt mixture was studied. It is found that with the increase of anti-stripping agent content, the penetration strength and Marshall stability of the cold patch asphalt mixture are increased gradually, while the diesel volatilization rate is decreased gradually. However, the immersion residual stability is increased first and then decreased with the increase of the dosage. When the dosage is 0.36 %, the immersion residual stability reaches the highest, which is 89.2 %. With increasing ratio of asphalt to diesel, the penetration strength and the immersion residual stability of the cold patch asphalt mixture are increased gradually. When the ratio of asphalt to diesel oil is more than 40∶7, the Marshall stability of the cold patch asphalt mixture is obviously enhanced, which is over 7 kN. However, the construction performance of the mixture is decreased. With increasing content of the cold patch, the penetration strength of the mixture is increased gradually. The Marshall stability, the diesel volatilization and the immersion residual stability of the cold patch asphalt mixture are decreased first and then increased with the increase of the dosage. When the dosage is 1.7%, the immersion residual stability reaches the highest, which is 89.6 %. Considering the Marshall performance and water stability of the cold patch asphalt mixture, the ratio of asphalt to diesel oil should be controlled to be 39∶10 with the cold patch asphalt additive of 1.7 % and the anti-stripping agent of 0.36 %.
作者 刘非易 李强 罗宵 沈凡 LIU Feiyi;LI Qiang;LUO Xiao;SHEN Fan(Materials Science and Engineering,Wuhan Institute of Technology,Wuhan 430205,China;Wuhan Municipal Construction Group Co.,Ltd,Wuhan 430023,China;Wuhan Municipal Construction Research Co.,Ltd,Wuhan 430024,China)
出处 《大连交通大学学报》 CAS 2021年第6期104-109,共6页 Journal of Dalian Jiaotong University
基金 武汉市市政建设集团有限公司科技计划资助项目(wszky201814)。
关键词 沥青冷补液 冷补沥青混合料 抗剥落剂 性能36 cold patch asphalt liquid asphalt mixture anti-stripping agent performance
  • 相关文献

参考文献10

二级参考文献39

  • 1凌建明,罗志刚,吕荔炫,袁文平.开挖路面结构修复三维有限元分析[J].同济大学学报(自然科学版),2006,34(7):886-890. 被引量:6
  • 2宋建生.储存式沥青混合料设计方法的研究[D].上海:同济大学,1997.
  • 3[1]Howard Lloyd Robinson, Derek Fordyce. Kadhim Khweir. Road Maintenance Using Cold Mix Material With Hot Mix Propeties, Eurasphlt & Eurobitume Congress 1996
  • 4[2]S. V. Shestoperov. Road and Building Materials, Mir Publishers, 1983
  • 5中华人民共和国交通部.TGF40-2004公路沥青路面施工技术规范[S].北京:人民交通出版社,2004.
  • 6中华人民共和国交通部.JTGF40-20H04公路沥青路面施工技术规范[S].北京:人民交通出版社,2004.
  • 7Wilson T P, Romine A R. Materials and procedures for repair of potholes in asphalt-surfaced pavernentsER]. Washington D C..U S Federal Highway Administration, 1999.
  • 8Berlin Marcus, Hunt Elizabeth. Asphalt concrete patching material evaluation [R]. Salem: Oregon Department of Transportation, 2001.
  • 9KALINOWSKI M L, LOWELL T C. Asphalt compositions[P]. USA Patent: US: 2759839, 1956-08-21.
  • 10RICHARDSON Ⅲ W A, ZIMIN S R A, FUEHOLZER J, et al. Tagging and identifying asphalt additives[P]. USA Patent:US 5306343, 1994-04-26.

共引文献137

同被引文献10

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部