小分子耐高温黏土稳定剂的制备与性能评价 被引量:4

Preparation and Performance Evaluation of a Small Molecular Clay Stabilizer with High Temperature Resistance
下载PDF
导出
摘要 针对无机盐类黏土稳定剂耐水洗效果差、聚合物类高分子黏土稳定剂易吸附阻塞孔道且耐温性能差等问题,采用三甲胺与γ-氯丙基三乙氧基硅烷制备小分子耐高温黏土稳定剂(ZWS-1)。评价了ZWS-1的防膨性能和耐温性能,考察了其与KCl的复配性能,并对其防膨机理进行了分析。结果表明,ZWS-1的最佳制备条件如下:反应物料硅烷与三甲胺物质的量比为1∶1.1、合成温度为90℃、反应时间为40 h、碘化钾用量为5%。ZWS-1的耐温性较好,最佳加量为1.5%。KCl可提高ZWS-1溶液的防膨率与耐水洗率。在150℃下,配方为1.5%ZWS-1+4%KCl的复配体系的黏土防膨率为98.3%、耐水洗率为91.4%。ZWS-1可以将黏土团聚为颗粒,增加黏土的稳定性;ZWS-1与黏土矿物表面的羟基发生脱水缩合反应,与黏土表面形成化学键起到了稳定黏土的作用。 In view of the problems of poor water washing resistance of inorganic salt clay stabilizer,easy adsorption and blocking of pores and poor temperature resistance of polymer clay stabilizer,a small molecular clay stabilizer(ZWS-1)with high temperature resistance was synthesized by using trimethylamine andγ-chloropropyl triethoxysilane.The anti-swelling performance and temperature resistance of ZWS-1 were evaluated.The synergistic effect of ZWS-1 and KCl was investigated.And the anti-swelling mechanism of ZWS-1 was analyzed.The results showed that the optimum preparation condition of ZWS-1 was obtained as follows:1∶1.1 the molar ratio of silane to trimethylamine,90℃synthesis temperature,40 h reaction time,and 5%potassium iodide.The temperature resistance of ZWS-1 was good and the optimum dosage of ZWS-1 was 1.5%.A synergistic effect was observed between 1.5%ZWS-1 and 4%KCl,whose anti-swelling rate was 98.3%,and the water washing resistance was91.4%at 150℃.ZWS-1 leaded to the agglomeration of clay particles and increased the stability of clay.The chemical bonds were formed through the dehydration condensation reaction between ZWS-1 and hydroxyl groups on the surface of clay,which played a role in stabilizing clay.
作者 申会兵 李媛媛 吴萍萍 张宏玉 SHEN Huibing;LI Yuanyuan;WU Pingping;ZHANG Hongyu(School of Chemical Engineering,China University of Petroleum(East China),Qingdao,Shandong 266580,P R of China)
出处 《油田化学》 CAS CSCD 北大核心 2021年第4期590-594,共5页 Oilfield Chemistry
关键词 黏土稳定剂 高温 低渗地层 有机硅烷 防膨率 耐水洗率 clay stabilizer high temperature low permeable formation organosilane anti-swelling rate water washing resistance
  • 相关文献

参考文献16

二级参考文献109

共引文献126

同被引文献50

引证文献4

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部