留置针连接管双层复合挤出工艺研究 被引量:3

Study on Double-layer Composite Extrusion Process for Indwelling Needle Connecting Tube
下载PDF
导出
摘要 采用热塑性聚氨酯弹性体(TPU)和聚氯乙烯(PVC)两种原材料(粒料),对留置针连接管进行双层复合挤出工艺研究。结果表明:由正交试验法确定的留置针连接管双层复合挤出的最佳工艺参数为TPU挤出输送段(一区)、熔融段(二区)、计量段(三区)、法兰和模具温度分别为170,173,180,178和178℃,挤出主机速度为15.0 r·min^(-1),牵引速度(牵引裁切机转速)为18 r·min^(-1);PVC挤出一区、二区、三区和法兰温度分别为168,170,175和173℃,挤出主机速度为15.0 r·min^(-1),牵引速度为18 r·min^(-1)。在最佳工艺参数条件下连续试生产留置针连接管8 h,抽检产品外直径的正态分析结果表明留置针连接管的双层复合挤出工艺稳定。 The double-layer composite extrusion process of the indwelling needle connecting tube was studied by using thermoplastic polyurethane elastomer(TPU)and polyvinyl chloride(PVC)as raw material(pellets).The results showed that,the optimum process parameters of the double-layer composite extrusion determined by orthogonal test were that the temperatures of TPU extrusion conveying section(zone 1),melting section(zone 2),metering section(zone 3),flange and die were 170,173,180,178 and 178℃respectively,the speed of extrusion host was 15.0 r·min^(-1),and the traction speed(traction cutting machine speed)was 18 r·min^(-1).The temperatures of PVC extrusion zone 1,zone 2,zone 3 and flange were 168,170,175 and 173℃respectively,the speed of extrusion host was 15.0 r·min^(-1) and the traction speed was 18 r·min^(-1).Under the optimum process parameters,the indwelling needle connecting tubes were continuously produced for 8 h,and the normal analysis results of the outer diameters of the sampled products showed that the double-layer composite extrusion process of the indwelling needle connecting tube was stable.
作者 程玲玲 赵明学 陈鹏涛 莫盼盼 牛富超 CHENG Lingling;ZHAO Mingxue;CHEN Pengtao;MO Panpan;NIU Fuchao(Henan Tuoren Medical Equipment Research Institute Co.,Ltd,Changyuan 453400,China)
出处 《橡胶工业》 CAS 2022年第5期374-379,共6页 China Rubber Industry
关键词 留置针连接管 双层复合挤出 工艺参数 热塑性聚氨酯弹性体 聚氯乙烯 正交试验法 indwelling needle connecting tube double-layer composite extrusion process parameter TPU PVC orthogonal test method
  • 相关文献

参考文献11

二级参考文献82

共引文献63

同被引文献53

引证文献3

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部