摘要
As the oxygen redox ability shows great effects on the catalytic performances of ceria-zirconia based materials,many strategies have been utilized to improve the oxygen storage capacity.Here in this study,we report a simple and facile approach to prepare a SO_(4)^(2-)-modified La,Y-doped ceria-zirconia material(SO/CZLY-f)with high oxygen storage capacity.Due to the additional redox process between SO_(4)^(2-)and S^(2-),oxygen storage capacity of SO/CZLY-f(745.3μmol O_(2)/g)is about 1.6 times higher than that of La,Ydoped ceria-zirconia material without SO_(4)^(2-)modification.Moreover,the catalytic activities and stability of the corresponding Pd-only three-way catalyst were measured.Compared to that of Pd@CZLY-f,the operation window of CO,full conversion temperature of HC and NO over Pd@SO/CZLY-f are obviously widened and lowered,respectively.After aging treatment at 1100℃for 4 h,the superiority of aged Pdloading composite is still maintained.
基金
Project supported by the Beijing Nova Program(Z181100006218030)
Major State Research Development Program of Hebei province(20374202D)。