TiB_(2)–Ni coatings with different binder phase contents were sprayed on Q235 substrate by a high-velocity oxygen-fuel(HVOF)method using ball-milled powders.The microstructure,phase compositions,as well as thermal shock behavior,abrasive wear,and corrosion resistance to molten Al-12.07 wt%Si alloy performances of as-sprayed coatings were investigated.The results show that the three TiB_(2)–Ni coatings structure is dense with low porosity,and the main phase compositions of the coatings are TiB_(2) and Ni similar to those of original powder.The coatings that have superior performance of thermal shock resistance have good bond to the substrate with no change in thick-ness and microstructure of coatings.Meanwhile,the coat-ings also have good durability in the molten Al-12.07 wt%Si after 60-h immersion test.And the mass loss of Q235 steel is five times as much as that of TiB_(2)–50Ni coatings after abrasive wear test.
出处
《Rare Metals》
SCIE
EI
CAS
CSCD
2022年第4期1385-1393,共9页
稀有金属（英文版）
基金
the National Natural Science Foundation of China(No.51001056)
the Natural Science Foundation of Jiangxi Province(No.20132BAB216014)
the Science and Technology Project of Jiangxi Educational Bureau(Nos.GJJ12610,GJJ13721,and GJJ12622)。