摘要
The incorporation of therapeutic-capable ions into bioactive glasses(BGs),either based on silica(SBGs)or phosphate(PBGs),is currently envisaged as a proficient path for facilitating bone regeneration.Inconjunction with this view,the single and complementary structural and bio-functional roles of CuO andGa_(2)O_(3)(in the 2e5 mol%range)were assessed,by deriving a series of SBG and PBG formulations startingfrom the parent glass systems,FastOs®BG e 38.5SiO2d36.1CaOd5.6P2O5d19.2MgOd0.6CaF2,and50.0P2O5d35.0CaOd10.0Na_(2)Od5.0 Fe2O_(3)(mol%),respectively,using the process of melt-quenching.The inter-linked physico-chemistry e biological response of BGs was assessed in search of bio-functional triggers.Further light was shed on the structural role e as network former or modifier e ofCu and Ga,immersed in SBG and PBG matrices.The preliminary biological performance was surveyedin vitro by quantification of Cu and Ga ion release under homeostatic conditions,cytocompatibility assays(in fibroblast cell cultures)and antibacterial tests(against Staphylococcus aureus).The similar(Cu)anddissimilar(Ga)structural roles in the SBG and PBG vitreous networks governed their release.Namely,Cuions were leached in similar concentrations(ranging from 10e35 ppm and 50e110 ppm at BG doses of 5and 50 mg/mL,respectively)for both type of BGs,while the release of Ga ions was 1e2 orders ofmagnitude lower in the case of SBGs(i.e.,0.2e6 ppm)compared to PBGs(i.e.,9e135 ppm).This wasattributed to the network modifier role of Cu in both types of BGs,and conversely,to the network former(SBGs)and network modifier(PBGs)roles of Ga.All glasses were cytocompatible at a dose of 5 mg/mL,while at the same concentration the antimicrobial efficiency was found to be accentuated by the coupledrelease of Cu and Ga ions from SBG.By collective assessment,the most prominent candidate material forthe further development of implant coatings and bone graft substitutes was delineated as the38.5SiO2d34.1CaOd5.6P2O5d16.2MgOd0.6CaF2d2.0CuOd3.0Ga_(2)O_(3)(mol%)SBG system,which yiel-ded moderate Cu and Ga ion release,excellent cytocompatibility and marked antibacterial efficacy.