摘要
Components and crystal structures of the intermetallic phases in a gravity die-cast Mg-6.0Zn-1.5Nd-0.5Zr(wt%)alloy were investigated using transmission electron microscopy.The results indicate that this alloy has multiple intermetallic phases and various inner faults.Totally,six eutectoid intermetallic phases,namely W(Mg Nd Zn_(3)),T(Mg_(39)Zn_(55)Nd_(6)),(Mg,Zr)Zn_(2),Z(Mg_(28)Zn_(65)Nd_(7)),H_(2)(Mg_(15)Zn_(70)Nd_(15)),and H1(Mg_(24)Zn_(64)Nd_(11)),were simultaneously observed at grain boundaries,and six precipitates(Z,Mg_(7)Zn_(3),T,Mg_(4)Zn_(7),β_(1)-Mg Zn_(2) and β_(2)-Mg Zn_(2))were found inα-Mg grains.Furthermore,faults like sub-grain boundaries,orientation domains(coherent with the same matching plane but with different orientations),stacking faults and twins were observed in the eutectoid intermetallic phases.Finally,some new orientation relationships between the known intermetallic phases were revealed.This paper can provide new insight into alloy design for Mg-Zn-RE(RE:rare earth)based alloys.
基金
supported by the National Natural Science Foundation of China under grants no.51701200 and 11804030
the Scientific and Technological Developing Scheme of Jilin Province under grants no.20200801048GH
the Project for Jilin Provincial Department of Education under grant no.JJKH20190583KJ。