Precipitation behaviors and mechanical properties of a solution-treated Mg-Gd-Nd-Zn-Zr alloy during equal-channel angular pressing process 被引量:4

下载PDF
导出
摘要 A magnesium alloy processed by equal-channel angular pressing (ECAP) exhibited excellent microstructure refinement and improved strength and hardness.The comprehensive mechanical properties of magnesium alloys have supported the expansion of their applications in the automotive,aerospace,and biomedical industries.Herein,pre-treatment of a solution-treated Mg-2.9Gd-1.5Nd-0.3Zn-0.3Zr alloy was conducted to investigate the precipitate behavior and microstructure evolution during the ECAP process.β;phase grains quickly precipitated from the solution-treated alloy,which accelerated grain refinement and enhanced the ductility after the ECAP process,as compared to the as-cast alloy reported in our previous study.Moreover,spherical precipitates (~200 nm) and fine phases (~100 nm) precipitated along the stripe-like Zn;Zr;phase,which formed a kabap-like structure dispersing homogeneously in the solution-treated alloy during the ECAP process.Owing to grain refinement,dislocations,sphericalβ;precipitates,and texture evolution,the solution-treated alloy after eight passes of ECAP exhibited good comprehensive mechanical properties,with the ultimate tensile strength,yield strength,and elongation values reaching210.9 MPa,263.9 MPa,and 27.9%,respectively.
出处 《Journal of Magnesium and Alloys》 SCIE EI CAS CSCD 2022年第1期257-266,共10页 镁合金学报(英文)
基金 financially supported by the Regional Joint Youth Fund Project of Guangdong Basic and Applied Basic Research(Grant No.2020A1515110619) Guangzhou Science and Technology Plan Project(Grant No.202002030356) the 2019 Youth Innovative Talents Project of General Colleges and Universities in Guangdong Province(Grant No.2019KQNCX106) the Talent Cultivation Project of Guangzhou University(Grant No.RP2020126)。
  • 相关文献

参考文献5

二级参考文献6

共引文献270

同被引文献35

引证文献4

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部