In this study,the effects of annealing and solution aging heat treatment on the microstructure and mechanical properties of cold spray additive manufactured(CSAMed)AA2024/Al_(2)O_(3) composite were investigated.The results showed that both annealing and solution aging enhanced the interfacial bonding between the deposited AA2024 particles in the composite.The tensile properties of CSAMed AA2024/Al_(2)O_(3) composite were significantly improved by 13.8%for ultimate tensile strength and 47.8%for elongation after solution aging.Microstructural examination and fractographic analysis showed that the fracture mechanism between the adjacent AA2024 particles changed from brittle to ductile-dominant mode after heat treatment.However,the interfacial bonding between the AA2024 and Al_(2)O_(3) particles cannot be improved.For the improvement of mechanical properties,the solution aging was slightly better than annealing.In addition,low-temperature annealing greatly reduced the anisotropy of the mechanical properties of CSAMed AA2024/Al_(2)O_(3) composite.
基金
supported by the National Natural Science Foundation of China (No.51875471)
the Research Fund of the State Key Laboratory of Solidification Processing (NPU),China (No.2021TZ-01)。