Tuning the reactivity of Al-Ni by fine coating of halogen-containing energetic composites 被引量:3

下载PDF
导出
摘要 In this paper,various core-shell structured Al—Ni@ECs composites have been prepared by a spray-drying technique.The involved ECs refer to the energetic composites(ECs)of ammonium perchlorate/nitrocellulose(AP/NC,NA)and polyvinylidene fluoride/hexanitrohexaazaisowurtzitane(PVDF/CL-20,PC).Two Al—Ni mixtures were prepared at atomic ratios of 1:1 and 1:3 and named as Al/Ni and Al/3Ni,respectively.The thermal reactivity and combustion behaviors of Al—Ni@ECs composites have been comprehensively investigated.Results showed that the reactivity and combustion performance of Al—Ni could be enhanced by introducing both NA and PC energetic composites.Among which the Al/Ni@NA composite exhibited higher reactivity and improved combustion performance.The measured flame propagation rate(v=20.6 mm/s),average combustion wave temperature(T_(max)=1567.0°C)and maximum temperature rise rate(γ_(t)=1633.6°C/s)of Al/Ni@NA are higher than that of the Al/Ni(v=15.8 mm/s,T_(max)=858.0°C,andγ_(t)=143.5°C/s).The enhancement in combustion properties could be due to presence of the acidic gaseous products from ECs,which could etch the Al_(2)O_(3)shell on the surface of Al particles,and make the inner active Al to be easier transported,so that an intimate and faster intermetallic reaction between Al and Ni would be realized.Furthermore,the morphologies and chemical compositions of the condensed combustion products(CCPs)of Al—Ni@ECs composites were found to be different depending on the types of ECs.The compositions of CCPs are dominated with the Al—Ni intermetallics,combining with a trace amount of Al_(5)O_(6)N and Al_(2)O_(3).
出处 《Defence Technology(防务技术)》 SCIE EI CAS CSCD 2022年第10期1810-1821,共12页 Defence Technology
基金 supported by the Nation Natural Science Foundation of China(Grant No.51776176) the Fundamental Research Funds for the Central Universities,China(Grant No.G2017KY0301) partially funded by NSAF project(Grant No.2030202) sponsored by Innovation Foundation for Doctor Dissertation of Northwestern Polytechnical University(Grant No.CX2021048)。
  • 相关文献

参考文献3

二级参考文献11

共引文献15

同被引文献24

引证文献3

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部