本文结合某厂500 kA电解系列长时间停产后再次复产时发现大量槽壳冷裂的特殊情况,从热应力及残余应力、温度和热疲劳等角度分析了槽壳破损的原因,讨论了破损机制,并提出了相应的修复方案。通过对此项工作的分析和讨论,希望给予其他企业一些借鉴和指导作用,提高电解槽的槽壳修复质量,延长槽壳使用寿命。
In this paper,based on special cases of a large number of pot shell cold cracks found in a restarted 500 kA pot line after a long period of shutdown,the causes for pot shell damages are analyzed from perspectives of thermal stress,residual stress,temperature and thermal fatigue,etc.,meanwhile,the damage mechanism is discussed,and the corresponding repair plan is also prorposed.Through analysis and discussion of this work,it's hoped that some reference and guidance could be provided for other enterprises,thus improving the repair quality and extending the service life of pot shells in aluminum reuction pots.