Enhancing strength and ductility in back extruded WE71 magnesium alloy cylindrical parts by introduction of multi-direction forging process 被引量:4

原文传递
导出
摘要 Magnesium cylindrical parts have relatively poor mechanical properties and distinct anisotropy of microstructure,which hinder their application as structural components.To improve the performance of WE71 cylindrical parts,multi-direction forging(MDF)was introduced before back extrusion,and the microstructure and mechanical properties were investigated.Results of microstructure show that the grain size in the outer of the cylindrical bottom is refined from 30.1 to 27.7μm,the micro structure is more uniform and the dislocation density is higher.The bimodal grain structure is formed in the outer of the cylindrical wall,which is ascribed to the formation of MgsRE phases along grain boundaries.These phases result in the Zener pinning effect on grain boundaries and the reduction of DRX volume fraction.The texture type of the cylindrical bottom is<0001>‖ED and the cylindrical wall is<1010>‖ED,and the maximum pole intensity is 1.986 and 1.664,respectively.Results of the tensile test at room temperature show that combined improved strength and ductility of the cylindrical part is attained after introducing the MDF process.The ultimate tensile strength(UTS),yield strength(YS)and elongation are279 MPa,185 MPa and 12%at the bottom and 299 MPa,212 MPa and 20%at the wall.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2023年第3期462-470,I0006,共10页 稀土学报(英文版)
基金 Project supported by the General Program of National Natural Science Foundation of China(51871195,51501015)。
  • 相关文献

同被引文献118

引证文献4

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部