摘要
Three kinds of Ce-based catalysts(CePO_(4),CeVO_(4),Ce_(2)(SO_(4))_(3))were synthesized and used for the selective catalytic reduction(SCR)of NO by NH_(3).NH_(3)-SCR performances were conducted in the temperature range of 80 to 400°C.The catalytic efficiencies of the three catalysts are as follow:CePO_(4)>CeVO_(4)>Ce_(2)(SO_(4))_(3),which is in agreement with their abilities of NH_(3)adsorption capacities.The highest NO conversion rate of CePO_(4)could reach about 95%,and the catalyst had more than 90%NO conversion rate between 260 and 320°C.The effect of PO_(4)^(3–),VO_(4)^(3–)and SO_(4)^(2–)on NH_(3)-SCR performances of Ce-based catalysts was systematically investigated by the X-ray photoelectron spectroscopy analysis,NH_(3)temperature programmed desorption,H2 temperature programmed reduction and field emission scanning electron microscopy tests.The key factors that can enhance the SCR are the existence of Ce4+,large NH_(3)adsorption capacity,high and early H2 consumptions,and suitable microstructures for gas adsorption.Finally,CePO_(4)and CeVO_(4)catalysts also exhibited relatively strong tolerance of SO2,and the upward trend about 8%was detected due to the sulfation enhancement by SO2 for Ce_(2)(SO_(4))3.
基金
This work was financially supported by the National Natural Science Foundation of China(Grant No.52102367)
And the tests of XRD and XPS were supported by Research and Test Center of Materials,Wuhan University of Technology
DRIFTS,TPD and TPR tests were supported by State Key Laboratory of Silicate Materials for Architectures,Wuhan University of Technology.