摘要
为了获得高品质的碱式硫酸镁晶须,采用氢氧化镁和七水硫酸镁为原料,通过水热法合成碱式硫酸镁晶须。考察了七水硫酸镁与氢氧化镁的物质的量比、水热时间、搅拌转速、七水硫酸镁的添加量及水热温度等条件因素对晶须生长的影响,利用X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、选区电子衍射(SAED)及傅里叶红外光谱(FT-IR)等对晶须产品进行了分析。结果表明:优化的工艺参数为七水硫酸镁与氢氧化镁物质的量比为3∶1、水热时间为2 h、搅拌转速为400 r/min、七水硫酸镁添加量为4.93 g、水热温度为180℃、80 mL水作为反应介质;在优化条件下合成的产品主要为纤维状晶须,晶须的直径为300~500 nm、长度为80~100μm,其长径比大于160。工艺参数的优化可有效提高碱式硫酸镁晶须的分散性和长径比。
To obtain the highquality basic magnesium sulfate whiskers,magnesium hydroxide and magnesium sulfate heptahydrate were used to prepare basic magnesium sulfate whiskers with the hydrothermal method.The influences of hydrothermal parameters on whisker morphology were investigated,which included the molar ratio of magnesium sulfate heptahydrate to magnesium hydroxide,hydrothermal time,stirring speed,addition amount of magnesium sulfate heptahydrate,and hydrothermal temperature.The whisker products were characterized by the various instruments of X-ray diffractometry(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),selected area electron diffraction(SAED),and Fouriertransform infrared spectrum(FT-IR).The results showed that the optimized process parameters were as following:the molar ratio of magnesium sulfate heptahydrate to magnesium hydroxide was 3∶1,hydrothermal time was 2 h,stirring speed was 400 r/min,addition amount of magnesium sulfate heptahydrate was 4.93 g,hydrothermal temperature was 180℃and the reaction medium of water was 80 mL.The products synthesized at the optimized conditions were mainly fibrous whiskers.The aspect ratio of fibrous whisker was more than 160 with the diameter of 300~500 nm and the length of 80~100μm.Therefore,the optimization of the process parameters could effectively improve the dispersion and aspect ratio of basic magnesium sulfate whiskers.
作者
蒋德敏
李顺梅
李青青
陈雨欣
刘代俊
JIANG Demin;LI Shunmei;Li Qingqing;Chen Yuxin;LIU Daijun(Key Laboratory of Water Environment Evolution and Pollution Control in Three Gorges Reservoir,Chongqing Three Gorges University,Chongqing 404100,China;School of Chemical Engineering,Sichuan University,Chengdu 6100653,China)
出处
《无机盐工业》
CAS
CSCD
北大核心
2023年第12期74-81,共8页
Inorganic Chemicals Industry
基金
重庆市教委科技项目(KJQN201901208)
重庆三峡学院青年项目(19QN04)
重点实验室开放项目(WEPKL2019YB07)。
关键词
碱式硫酸镁晶须
水热法
形貌
氢氧化镁
七水硫酸镁
basic magnesium sulfate whisker
hydrothermal method
morphology
magnesium hydroxide
magnesium sulfate heptahydrate