摘要
A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourier-transform infrared)spectroscopy,SEM(Scanning electron microscopy)and in terms of water contact angles.Its oil-water absorption and separation capacities were measured by FT-IR and UV-visible spectrophoto-metry.The experimental results have shown that oligomeric silanol covalently bonds by Si-N onto the surface of melamine sponge skeletons.SMS has shown superhydrophobicity with a water contact angle exceeding 150°±1°,a better separation efficiency with regard to diesel oil(by 99.31%(wt/wt%)in oil-water mixture and even up to 99.99%(wt/wt%)for diesel oil in its saturated aqueous solution.Moreover,SMS inherited the intrinsicflame retardancy of the melamine sponge.In general,SMS has shown superhydrophobicity,high porosity,excellent selectivity,remarkable recyclability,and better absorption capacity for various oils and organic solvents,and a high separation efficiency for oil in saturated aqueous solutions.
基金
funded by Qingyang Science and Technology Support Project(KT2019-03)。