磷化工艺对FeSiCr软磁复合材料磁性能的影响 被引量:1

Influence of phosphating process on magnetic properties of FeSiCr soft magnetic composites
原文传递
导出
摘要 采用锌锰磷化液对FeSiCr合金粉末进行表面改性处理,通过振动样品磁强计、阻抗分析仪和软磁材料交流测试装置分析锌锰磷化液浓度对FeSiCr磁粉饱和磁化强度、FeSiCr磁粉芯有效磁导率和功率损耗的影响。结果表明,随着锌锰磷化液浓度的增加,样品的饱和磁化强度逐渐减小,功率损耗先减小后增大。当锌锰磷化液浓度为25%时,有效磁导率为39.5,功率损耗仅为103.6 W·kg^(-1)(100 kHz,50 mT)。 In this study,the surface modification treatment of FeSiCr alloy powder was carried out with zinc-manganese phosphating solution.Vibrating sample magnetometer,impedance analyzer and soft magnetic material AC test device were used to analyze effects of the content of zinc-manganese phosphating solution on saturation magnetization of FeSiCr magnetic powder,effective permeability and power loss of FeSiCr magnetic powder cores.The results show that with the increase of the concentration of zinc-manganese phosphating solution,the saturation magnetization of the composite magnetic powder core gradually decreases,the power loss first decreases and then increases.When the concentration of zinc-manganese phosphating solution is 25%,the effective permeability is 39.5,and the power loss is only 103.6 W·kg^(-1)(100 kHz,50mT).
作者 何正烨 罗剑 安静 徐立红 牟星 郭世海 HE Zhengye;LUO Jian;AN Jing;XU Lihong;MU Xing;GUO Shihai(Department of Functional Material Research,Central Iron and Steel Research Institute,Beijing 100081,China)
出处 《粉末冶金工业》 CAS 北大核心 2024年第2期86-90,96,共6页 Powder Metallurgy Industry
关键词 FeSiCr磁粉芯 锌锰磷化液 饱和磁化强度 有效磁导率 功率损耗 FeSiCr magnetic powder core zinc-manganese phosphating solution saturation magnetization effectivepermeability coreloss
  • 相关文献

参考文献10

二级参考文献152

共引文献50

同被引文献6

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部