摘要
Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%,5%,10%,15%,20%,25%,30%,35%,40%,45%,50%Cu-coated Fe were prepared in mesh belt sintering furnace.Microscopic pore morphology of materials was observed,bending strength was tested.Results show that,There is a good bonding between Cu-coated Fe and CuSn10,with the increase of Cu-coated Fe content from 0%to 50%,bending strength of bilayer composite materials increases.