摘要
Morphotropic phase boundary(MPB)-based ceramics are excellent for energy harvesting due to their enhanced physical properties at phase boundaries,broad operating temperature range,and ability to customize properties for efficient conversion of mechanical energy into electrical energy.In this work,Bi_(1–x)Na_(x)Fe_(1–x)Nb_(x)O_(3)(x=0.20,0.30,0.32 and 0.40,BNFNO abbreviation)based ceramics were synthesized using a solid-state route and blended with Polydimethylsiloxane(PDMS)to achieve flexible composites.Various material characterization and energy harvesting were performed by designing a hybrid piezoelectric(PENG)-triboelectric(TENG)device.The voltage and current of PENG,TENG,and hybrid bearing same device area(2 cm×2 cm)were recorded as 11 V/0.3μA;60 V/0.7μA;110 V/2.2μA.The strategies for enhancing the output performance of the hybrid device were evaluated,such as increased surface area(creating micro-roughness and porous morphology)and increasing electrode size and multi-layer hybrid device formation.The self-powered acceleration monitoring was demonstrated using the hybrid device.Further,the low-frequency-based wave energy is converted into electrical energy,confirming the usage of hybrid PENG-TENG devices as a base for battery-free sensors and blue energy harvesting.
基金
This work is supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)(2021R1C1C1011588)
funded by the Ministry of Science and ICT of Korea.HJ Kim was supported by the Ministry of Trade,Industry and Energy of Korea(RS-2023-00231350)
YKM acknowledges the funding by Interreg Deutschland-Denmark with money from the European Regional Development Fund,project number 096-1.1-18(Access and Acceleration)
N.Vittayakorn was funded by KMITL under grant No.KREF11650
Z Jagličićwas supported by the Slovenian Research Agency(Grant No.P2-0348).