Piezoelectric PZT ceramics with high piezoelectric properties and good thermal stability are urgently desired concerning the practical application.New compositions of LiNbO_(3) modified Pb(Ni_(1/3)Nb_(2/3))O_(3)single bondPbZrO_(3)single bondPbTiO_(3) ceramics have been prepared in this study.The effects of the introduction of the LiNbO_(3) on the system were comprehensively investigated in terms of the phase structure,microstructure,electric properties,and thermal stability behavior of the ceramics.All compositions are located in the morphotropic phase boundary(MPB)region,and the ratio of the rhombohedral(R)phase increases obviously with the increase of LiNbO_(3) concentration.With increasing the LiNbO_(3) content,the piezoelectric properties were significantly enhanced.The sample added with 2%(in mole)LiNbO_(3) shows excellent electric properties,including T_(m)=185℃,εr=5,643,k_(p)=0.626,Q_(m)=51,d_(33)=902 pC/N.More importantly,no thermal depolarization behavior was observed in the temperature range of 25–100℃.For PNN-PZT-x%LN ceramics,which is mainly attributed to the pinning effect resulted by the(Li_(Pb)-Nb_(Zr/Ti)) defect dipoles.
基金
This work was supported by Key Research and Development Program of Ministry of Science and Technology of China(No.2022YFB3204000).