This study focuses on developing a novel multiphase stainless steel with enhanced ductility and an ultralow yield ratio achieved through solid-solution treatment.The steel exhibits remarkable mechanical properties:a tensile strength of approximately 1114 MPa,an ultralow yield ratio of 0.36,exceptional uniform elongation of approximately 17.48%,and total elongation of approximately 21.73%.The remarkable ductility of the steel can be attributed to the transformation-induced plasticity(TRIP)effect observed in the retained austenite,while its exceptional strength results from the combined effects of TRIP and the martensite phase.