某超临界锅炉水冷壁多处泄漏原因分析

Analysis on Multiple Leakages Causes in Water Wallof a Supercritical Boiler
下载PDF
导出
摘要 某超临界锅炉水冷壁螺旋管区域发生多处泄漏,对泄漏管取样后进行了宏观检查、化学成分、金相组织和拉伸性能等分析.结果表明:原始泄漏点处于水冷壁管鳍片焊缝熔合区,鳍片焊缝存在大量焊接缺陷导致产生该泄漏点;泄漏的汽水流将相邻管吹损,相邻管出现多处次生漏点,造成管内介质流量降低,导致在次生漏点的下游区域发生短时过热爆管.建议应严格控制和检查鳍片焊缝的焊接质量. The spiral tube of the water wall of a supercritical boiler was leaked in many places.After sampling the leakage tube,the macroscopic examination,chemical composition,metallographic structure and tensile properties were analysed.Results show that,the original leakage point is located in the fusion zone of the water wall tube fin weld,which is caused by a large number of welding defects in the fin weld.The leakage of steam water blows adjacent pipe.The adjacent pipe appears multiple secondary leakage points,and the medium flow rate in adjacent pipe is reduced,resulting in short-term overheating in the downstream area of the secondary leakage points.It is recommended that the welding quality of fin welds should be strictly controlled and checked.
作者 董鹏 盛金贵 田成川 Dong Peng;Sheng Jingui;Tian Chengchuan(Huadian Electric Power Research Institute Co.,Ltd.,Huhhot 010020,China)
出处 《发电设备》 2024年第6期389-392,共4页 Power Equipment
关键词 超临界锅炉 水冷壁 鳍片焊缝 焊接缺陷 短时过热 supercritical boiler water wall fin weld weld defect short-term overheating
  • 相关文献

参考文献4

二级参考文献30

共引文献17

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部