低碳高强度双相钢丝内耗行为的试验研究 被引量:1

Inner-consumption of Low Carbon High Strength Dual-Phase Steel Wire
下载PDF
导出
摘要 研究了 2 0钢双相钢丝的内耗行为 ,结果表明 ,双相钢丝的内耗曲线上存在 2 2 0℃内耗峰 。 The performance of inner-consumption of dual-phase wire made of steel 20 was researched.Conclusion was drown: there is a peak in the path of inner-consumption curve at 220℃, the changing tendency of the peak height of inner-consumption and the tensile strength of steel wire is similar generally.
出处 《济南大学学报(自然科学版)》 CAS 2002年第4期349-351,共3页 Journal of University of Jinan(Science and Technology)
关键词 低碳高强度双相钢丝 内耗行为 试验研究 抗拉强度 变形行为 断裂机制 dual-phase steel wire tensile strength inner-consumption
  • 相关文献

参考文献5

  • 1王晓敏.绳用低碳双相钢丝开发试验研究[J].金属制品,1986,2(6):2-8.
  • 2朱雅年.20双相钢的组织与性能[J].上海金属,1983,5(2):39-44.
  • 3Lanzillotto C A N. Structure - property relationships in dualphase steels[J ]. Metal Science, 1982,6 (8): 371 ~ 381.
  • 4Jiang Z G. Effects of microstructural variables on the deformation behaviour of dual- phase steel. Materials Science and Engineering, 1995, A190 ( 1 ): 55 ~ 64.
  • 5谢超英.普通中碳钢双相钢丝的组织与性能[D].哈尔滨:哈尔滨工业大学,1986.

共引文献3

同被引文献3

  • 1王晓敏.绳用低碳双相钢丝开发试验研究[J].金属制品,1986,2(6):2-8.
  • 2朱雅年.20双相钢的组织与性能[J].上海金属,1983,5(2):39-44.
  • 3Jiang Z G,et al,Effects of microstructural variables on the deform ation behaviour of dual-phase steel[J].Macterial Science and Engineering,1995,A 190(1):55-64.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部