锐钛矿型纳米TiO_2介孔粉体表面织构的研究 被引量:23

Surface Texture of Nanometer Mesoporous Titania Powders
下载PDF
导出
摘要 以硫酸钛和尿素为原料 ,聚乙二醇 -1 0 0 0为空间构造剂 ,1 0 4℃下经尿素水解均匀沉淀法研制颗粒分散均匀、粒径可控的高热稳定性锐钛矿型纳米 Ti O2 介孔粉体 ,并对其晶相、颗粒大小、比表面积、形貌和孔道结构进行了表征 .结果表明 ,未经任何热处理的 Ti O2 粉体即为锐钛型晶相 ,颗粒为均匀分散的类球型颗粒 ,且颗粒间形成直通型的介孔孔道 ,其孔径在 1 0~ 30 nm之间 .控制焙烧温度可以达到控制颗粒大小及形貌的目的 ,经 85 0℃焙烧 5 h的样品仍保持锐钛矿型晶相 ,未出现向金红石型晶相转变的迹象 . Nanometer titania mesoporous powders were prepared by heating the mixed solution of titanium disulfate and polyethylene glycol(PEG-1000) in the presence of urea under hydrothermal conditions at 104 ℃.The texture, morphology and crystallite size of the synthesized nanoparticle powders were investigated by XRD, BET, TEM and DSC. The powders dried at room temperature and calcined at temperature below 850 ℃, their particles were spherical, well dispersed, ultrafine titania, with anatase phase. Their crystallite size increased from 8.56 to 48.82 nm with increasing the calcining temperature from room temperature to 850 ℃.The pore structure among particles, open-ended tubular pores, were mesoporous texture, the average pore diameters were from 10.36 to 27.25 nm.
出处 《高等学校化学学报》 SCIE EI CAS CSCD 北大核心 2003年第1期146-150,共5页 Chemical Journal of Chinese Universities
基金 教育部科学技术研究重点项目 (批准号 :0 0 0 16 )资助
关键词 TiO2 介孔材料 锐钛矿 纳米二氧化钛 水解 硫酸钛 尿素 均匀沉淀 Mesoporous powder Anatase Nano-titania
  • 相关文献

参考文献2

  • 1余家国 赵修建.Chem. J. Chinese Universities(高等学校化学学报)[J],2000,21(9):1-1.
  • 2严瑞.Water-soluble Polymers(水溶性高分子)[M].Beijing: Chemical Technology Press,2000.223-230.

共引文献2

同被引文献245

引证文献23

二级引证文献126

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部