合成甲醇的催化剂Rh-ZnO/MWNTs的研究 被引量:7

Study on Rh ZnO/MWNTs Catalyst for Methanol Synthesis
下载PDF
导出
摘要 研究新型的由多壁碳纳米管(MWNTs)负载的,ZnO助催的铑基甲醇合成催化剂.当铑含量达到4%(w)时,催化剂具有较高的比表面积(99.6m2·g-1),催化剂的反应活化能为68.8kJ·mol-1.在563K,1MPa下,催化剂的最高催化活性和甲醇选择性分别为411.4mg/gcat.·h和96.7%.TEM、TPR和TPD等表征结果显示,碳纳米管能增加Rh在催化剂表面的分散度,提高催化剂的还原温度并能增加氢物种的吸附量,这些结果将有助于更好地了解催化剂中各组分间的协同作用和催化活性中心本质. A novel catalyst for methanol synthesis, ZnO-promoted rhodium supported on multi-wall carbon nanotubes(MWNTs), was developed. As Rh content in catalyst is 4% (w), the catalyst has higher specific surfafic area of 99.6m(2) (.) g(-1) and activation energy of 68.8 kJ (.) mol(-1). The highest catalytic activity of CH3OH, 411.4 mg/gcat (.) h, can be obtained at 563 K and under 1 MPa (Table 1.). The results of TEM, TPR and TPD showed that MWNTs can enhance the dispersion degree of Rh on the catalyst surface, increase the reduction temperature of the catalyst and the adsorption capacity of hydrogen species. These results will contribute to a better understanding of the synthergistic action of reaction components and the nature of catalytic activity center in the catalyst.
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 2003年第1期65-69,共5页 Acta Physico-Chimica Sinica
基金 福建省自然科学基金(E9910001 E0010006)资助项目~
关键词 Rh-ZnO/MWNTs 甲醇 合成 铑基催化剂 多壁碳纳米管 反应机理 负载型催化剂 氧化锌 methanol synthesis Rh catalyst multi-wall carbon nanotubes(MWNTs) hydrogen storing
  • 相关文献

参考文献1

二级参考文献5

  • 1陈鸿博,厦门大学学报,1990年,29卷,4期,411页
  • 2陈鸿博,1988年
  • 3刘忠惠,光电子能谱及其在催化中的应用,1987年
  • 4陈鸿博,博士学位论文,1986年
  • 5Briggs D,X-射线与紫外光电子能谱,1984年

共引文献5

同被引文献209

引证文献7

二级引证文献72

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部