摘要
采用等体积浸渍法制备了CeO2 /Al2 O3、CeO2 /TiO2 复合氧化物载体 .应用X 射线粉末衍射 (XRD)、比表面积测定、激光Raman光谱、扫描电子显微镜 (SEM )等技术研究了CeO2 在Al2 O3及TiO2 载体上的分散状态 .结果显示 :对CeO2 /Al2 O3,CeO2 主要存在于Al2 O3表面 ,晶粒小、分散性好 ;而对CeO2 /TiO2 ,大部分CeO2 以体相形式与TiO2 共存 ,晶粒大、分散性也差 .此外 ,也没有发现TiO2 由锐钛矿向金红石的晶相变化 .CeO2 /Al2 O3具有比Ce/TiO2 更大的比表面积 。
CeO 2 modified Al 2O 3 and TiO 2 supports are prepared using incipient wet impregnation method. X ray diffraction (XRD), surface areas measurement, laser Raman spectroscopy, and scanning electron microscopy (SEM) are employed to study the dispersion of CeO 2 on Al2O 3 and TiO 2. The results indicate that CeO 2 has small particles with good dispersion on Al 2O 3 surface for CeO 2/Al 2O 3. However, CeO 2 phase coexists mainly with TiO 2 phase in CeO 2/TiO 2. Phase transformation from anatase to rutile of TiO 2 is not observed for CeO 2/TiO 2 sample. CeO 2/Al 2O 3 has larger specific surface area and then is more suitable as catalysts support.
出处
《烟台大学学报（自然科学与工程版）》
CAS
2003年第1期49-53,共5页
Journal of Yantai University(Natural Science and Engineering Edition)
基金
山东省教委资助课题 (J97C5 5 )