摘要
In this communication,we report a synthetic approach to fabricate Y-junction Co nanowires and Y-junction Cu nanowires by AC electrodeposition using a hierarchically designed anodized aluminum oxide template.Morphology study showe that diameters of the stems and branches of the Y-junction nanowires were about 40 nm and 20 nm respectively.Structural analysis indicates that Co nanowires had a mixture of face-center-cubic and hexagonal-close-packed structures,whereas Cu nanowires had a face-center-cubic structure with a <110> texture.The Y-junction Co nanowires exhibited a longitudinal coercivity of 1300 Oe and remnant magnetization of 56%,which was affected by the growth direction and microstructure.The present method can be extended to other metallic systems and thus provides a simple and efficient way to fabricate Y-junction metal nanowires.
In this communication,we report a synthetic approach to fabricate Y-junction Co nanowires and Y-junction Cu nanowires by AC electrodeposition using a hierarchically designed anodized aluminum oxide template.Morphology study showe that diameters of the stems and branches of the Y-junction nanowires were about 40 nm and 20 nm respectively.Structural analysis indicates that Co nanowires had a mixture of face-center-cubic and hexagonal-close-packed structures,whereas Cu nanowires had a face-center-cubic structure with a <110> texture.The Y-junction Co nanowires exhibited a longitudinal coercivity of 1300 Oe and remnant magnetization of 56%,which was affected by the growth direction and microstructure.The present method can be extended to other metallic systems and thus provides a simple and efficient way to fabricate Y-junction metal nanowires.
基金
financially supported partially by a NSF award CMMI-0825990