Coral-Like Yolk–Shell-Structured Nickel Oxide/Carbon Composite Microspheres for High-Performance Li-Ion Storage Anodes 被引量:5

下载PDF
导出
摘要 In this study, coral?like yolk–shell?structured NiO/C composite microspheres(denoted as CYS?NiO/C) were prepared using spray pyrolysis. The unique yolk–shell structure was characterized, and the formation mechanism of the structure was proposed. Both the phase separation of the polyvinylpyrrolidone and polystyrene(PS) colloidal solution and the decompo?sition of the size?controlled PS nanobeads in the droplet played crucial roles in the formation of the unique coral?like yolk–shell structure. The CYS?NiO/C microspheres delivered a reversible discharge capacity of 991 mAh g^(-1) after 500 cycles at the current density of 1.0 A g^(-1). The dis?charge capacity of the CYS?NiO/C microspheres after the 1000 th cycle at the current density of 2.0 A g^(-1) was 635 mAh g^(-1), and the capacity retention measured from the second cycle was 91%. The final discharge capacities of the CYS?NiO/C microspheres at the current densities of 0.5, 1.5, 3.0, 5.0, 7.0, and 10.0 A g^(-1) were 753, 648, 560, 490, 440, and 389 mAh g^(-1), respectively. The synergetic e ect of the coral?like yolk–shell structure with well?defined interconnected mesopores and highly conductive carbon resulted in the excellent Li+?ion storage properties of the CYS?NiO/C microspheres. In this study, coral?like yolk–shell?structured NiO/C composite microspheres(denoted as CYS?NiO/C) were prepared using spray pyrolysis. The unique yolk–shell structure was characterized, and the formation mechanism of the structure was proposed. Both the phase separation of the polyvinylpyrrolidone and polystyrene(PS) colloidal solution and the decompo?sition of the size?controlled PS nanobeads in the droplet played crucial roles in the formation of the unique coral?like yolk–shell structure. The CYS?NiO/C microspheres delivered a reversible discharge capacity of 991 mAh g^(-1) after 500 cycles at the current density of 1.0 A g^(-1). The dis?charge capacity of the CYS?NiO/C microspheres after the 1000 th cycle at the current density of 2.0 A g^(-1) was 635 mAh g^(-1), and the capacity retention measured from the second cycle was 91%. The final discharge capacities of the CYS?NiO/C microspheres at the current densities of 0.5, 1.5, 3.0, 5.0, 7.0, and 10.0 A g^(-1) were 753, 648, 560, 490, 440, and 389 mAh g^(-1), respectively. The synergetic e ect of the coral?like yolk–shell structure with well?defined interconnected mesopores and highly conductive carbon resulted in the excellent Li+?ion storage properties of the CYS?NiO/C microspheres.
出处 《Nano-Micro Letters》 SCIE EI CAS CSCD 2019年第1期46-63,共18页 纳微快报(英文版)
基金 supported by the National Research Foundation of Korea (NRF) Grant funded by the Korea government (MSIP) (NRF-2018R1A4A1024691, NRF-2017M1A2A2087577, and NRF-2018R1D1A3B07042514)
  • 相关文献

二级参考文献3

共引文献11

同被引文献19

引证文献5

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部