摘要
The MAO (Micro-Arc Oxidation) process is applied to a eutectic Al-Si alloy(Al-12.0 percent Si-l.0 percent Cu-0.9 percent Mg (mass fraction)). The oxide ceramic layer wasfabricated with about 220 mum thickness and 3000 Hv micro-hardness. By XRD (X-ray diffractometry)and DSC (differential scanning calorimetry) analyses, the oxide layer consists of amorphous Al_2O_3,which is distinct from the results reported by the other researchers. The SEM photographs of suchlayer show that the layer is fixed tightly on the substrate alloy. So this alloy can he used in thehigh temperature and friction environment alter it is treated with such process.
The MAO (Micro-Arc Oxidation) process is applied to a eutectic Al-Si alloy(Al-12.0 percent Si-l.0 percent Cu-0.9 percent Mg (mass fraction)). The oxide ceramic layer wasfabricated with about 220 mum thickness and 3000 Hv micro-hardness. By XRD (X-ray diffractometry)and DSC (differential scanning calorimetry) analyses, the oxide layer consists of amorphous Al_2O_3,which is distinct from the results reported by the other researchers. The SEM photographs of suchlayer show that the layer is fixed tightly on the substrate alloy. So this alloy can he used in thehigh temperature and friction environment alter it is treated with such process.
基金
This project is financially supported by the National Natural Science Foundation of China (No. 50071028)
the Natural Science Foundation of Shandong Province (No. L2000F01)