摘要
论文进行了粉煤灰对外掺氧化镁混凝土压蒸膨胀变形和孔隙结构影响的试验研究。结果表明,粉煤灰的掺入使混凝土的压蒸膨胀率降低,但粉煤灰掺量超过30%后,降低的幅度减小。粉煤灰的掺入使混凝土平均孔径细化,无害孔隙和少害孔隙的比例增大,混凝土的孔隙构造得到改善。MgO掺量越大,粉煤灰对混凝土的压蒸膨胀率的抑制作用越明显;同时,随着MgO掺量的增大,粉煤灰对混凝土的平均孔径的改善也越明显。
The influence of fly ash content on the autoclave-treated expansibility and pore parameters of concrete mixed with MgO are tested. The results show that the autoclave-treated expansibility of concrete with fly ash is re- duced, but the range of reducing is reduced when the fly ash content passes 30 percent. The average in size of aperture is refined, and the proportion of innocuous and less harmful pore is increased, meanwhile, the pore structure is im- proved of concrete with fly ash. The more obvious inhibitory effect to the autoclave-treated expansibility and the more obvious improvement to the average in size of aperture with MgO content increasing.
出处
《膨胀剂与膨胀混凝土》
2013年第4期15-19,共5页
Expansive Agents & Expansive Concrete
关键词
水工混凝土
压蒸膨胀率
孔隙结构参数
试验研究
hydraulic mass concrete
autoclave-treated expansibility
parameters of pore structure
experimental research