Sm_2 Fe_(17) prepared by reduction-diffusion method needs to be washed with water to remove calcium oxide. Electrochemical corrosion occurs when Sm_2 Fe_(17) powder is in contact with liquid water. Corrosion mechanism of H_2 O on Sm_2 Fe_(17) powder and nitrogenation process of corroded Sm_2 Fe_(17) were studied by analyzing the structure and morphology. It is indicated that the metallic hydroxide forms and deposits on the Sm_2 Fe_(17) powder surfaces during water corrosion. At the same time, oxygen and hydrogen enter the unit cell of Sm2 Fe_(17), causing a slight increase in Curie temperature. In the subsequent nitriding process,the hydroxide is dehydrated and hydrogen is desorbed. The resulting oxide reacts with Sm_2 Fe_(17)N_x to form a-Fe and Sm_2 O_3. Thermodynamic calculations using the HSC Chemistry 6.0 software indicate that the reaction can occur spontaneously. The effect of water corrosion on the magnetic properties of the nitride can be eliminated by hydrogen reduction prior to nitriding.
Sm_2 Fe_(17) prepared by reduction-diffusion method needs to be washed with water to remove calcium oxide. Electrochemical corrosion occurs when Sm_2 Fe_(17) powder is in contact with liquid water. Corrosion mechanism of H_2 O on Sm_2 Fe_(17) powder and nitrogenation process of corroded Sm_2 Fe_(17) were studied by analyzing the structure and morphology. It is indicated that the metallic hydroxide forms and deposits on the Sm_2 Fe_(17) powder surfaces during water corrosion. At the same time, oxygen and hydrogen enter the unit cell of Sm2 Fe_(17), causing a slight increase in Curie temperature. In the subsequent nitriding process,the hydroxide is dehydrated and hydrogen is desorbed. The resulting oxide reacts with Sm_2 Fe_(17)N_x to form a-Fe and Sm_2 O_3. Thermodynamic calculations using the HSC Chemistry 6.0 software indicate that the reaction can occur spontaneously. The effect of water corrosion on the magnetic properties of the nitride can be eliminated by hydrogen reduction prior to nitriding.
基金
Project supported by Natural Science Foundation of Ningbo,China(2017A610079)
Technology Innovation&Achievement Industrialization Project of Ningbo China(2014B11010)