PBAT/PLA薄膜的制备及性能研究 被引量:21

Preparation and Properties of PBAT/PLA Film
下载PDF
导出
摘要 将聚乳酸(PLA)和聚对苯二甲酸-己二酸-丁二醇酯(PBAT)共混制备成共混材料,探讨了不同PLA含量对材料性能的影响。结果表明,PBAT/PLA共混材料中,随着PLA含量的增加,拉伸强度先降低后升高,当PLA含量为90%时,拉伸强度达到60.12 MPa,而其断裂伸长率从703%降低至8%,由韧性材料逐渐转变为脆性材料;PLA含量为30%时,性能变化出现拐点;PLA含量为50%时出现明显相分离,且PLA的加入可以加速PBAT材料的结晶,使结晶温度由38℃提高至82℃;PBAT/PLA共混材料在PLA含量低于70%时,都可以实现较好的吹膜过程,且薄膜材料的拉伸强度为39.59 MPa,断裂伸长率不低于137%。 In this study,blends from poly(lactic acid)(PLA) and polybutyleneadipate-coterephthalate(PBAT) was fabricated and the mechanical and bio-degradation properties were studied.It showed that with increasing PLA content,the tensile strength of PBAT/PLA blends increased firstly and then decreased,the elongation at break decreased continuously,and the blends underwent a ductile-brittle transition.When PLA content reached 30 wt%,a mechanical property change point occurred.When PLA content reached 50%,phase separation took place.The addition of PLA could accelerate the crystallization rate of PBAT,which increased the crystallization temperature from 38 C to 82 C.PBAT/PLA film could be fabricated with good mechanical property only if PLA content was below 70%.
出处 《中国塑料》 CAS CSCD 北大核心 2015年第3期45-50,共6页 China Plastics
关键词 聚对苯二甲酸-己二酸-丁二醇酯 聚乳酸 力学性能 生物降解性能 相容性 polybutyleneadipate-co-terephthalate poly(lactic acid) mechanical property biodegradale property compatibility
  • 相关文献

参考文献10

二级参考文献40

  • 1陈宇宏,袁渊,郭宝华.聚碳酸酯与聚酯的相容性研究[J].工程塑料应用,2004,32(6):4-7. 被引量:8
  • 2顾书英,詹辉,任杰.聚乳酸/PBAT共混物的制备及其性能研究[J].中国塑料,2006,20(10):39-42. 被引量:64
  • 3朱兴吉,顾书英,任杰,詹辉.PEG对PLA/Ecoflex复合材料性能的影响[J].塑料工业,2007,35(7):19-21. 被引量:10
  • 4朱诚身.聚合物结构分析[M].北京:科学出版社,2005.40.
  • 5GUPTA A P, KUMAR V. New emerging trends in synthetic biodegradable polymers-polylactide: a critique [ J ]. Eur Polym J, 2007, 43 (10): 4053-4074.
  • 6JEON O, LEE S H, KIM S H. Synthesis and characterization of poly (L-lactide) - poly (ε-caprolactone) multiblock copolymers [ J ]. Macromolecnles, 2003, 36: 5585 - 5592.
  • 7SCHRECK K M, HILLMYER M A. Block copolymers and melt blends of poly lactide with Nodax ^TM microbial polyesters: preparation and mechanical properties [ J ]. J Biotechnol,2007, 132:287 -295.
  • 8COLTELLI M B, DELLA M I, BERTOLDO M, et al. Poly (lactic acid) properties as a consequence of poly (butylene adipate-co-terephthalate) blending and acetyl tributyl citrate plasticization [ J]. J Appl Polym Sci, 2008, 110 (2) : 1250 - 1262.
  • 9JIANG L, WOLCOTT M P, ZHANG J. Study of biodegradable polylactide/poly ( butylene adipate-co-terephthalate ) blends [J]. Biomacromolecules, 2006, 7 (1): 199-207.
  • 10LIN Y, ZHANG K Y, DONG Z M, et al. Study of hydrogen-bonded blend of polylactide with biodegradable hyperbranched poly (ester amide) [ J]. Macromolecules, 2007, 40 (17) : 6257 -6267.

共引文献38

同被引文献185

引证文献21

二级引证文献132

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部