摘要
针对某钢厂生产的DP590钢的工艺流程(高炉炼铁→BOF→LF精炼→连铸),分析了各工序以及铸坯中T[O]、T[N]和显微夹杂物的类型、来源、数量及组成。结果表明,稳态铸坯中T[O]=28×10^(-6),T[N]=29×10^(-6),显微夹杂的数量为8个/mm^2,显微夹杂类型主要有:CaS-Al_2O_3类夹杂、CaO-Al_2O_3类夹杂、Al_2O_3类夹杂、CaS类夹杂;粒度分别在1～10μm、4～20μm、1～4μm、1～10μm,含量分别为50%、20%、20%、10%。
The type,source,quantity and composition of T[O],T[N]and microinclusions in the billet of DP590 steel(blast furnace ironmaking,BOF,LF refining,continuous casting)were analyzed.The results show that the steady state slab of T[O]=25×10-6,T[N]=27×10-6,the number of micro-inclusions is 8 p/mm-2,the types of microscopic inclusions are as follows:CaS-Al2O3,CaO-Al2O3,Al2O3 and CaS.Particle sizes range from 1~10μm,4~20μm,1~4μm,1~10μm,and the content are 50%,20%,20%,10%,respectively.
作者
周景一
刘文慧
肖鹏程
张彩军
胡海亮
ZHOU Jingyi;LIU Wenhui;XIAO Pengcheng;ZHANG Caijun;HU Hailiang(School of Metallurgy&Energy,North China University of Science and Technology,Tangshan 063210,China;Hebei Province High Quality Steel Continuous Casting Engineering Technology Research Centre,Tangshan 063000,China;School of Economics,North China University of Science and Technology,Tangshan 063210,China)
出处
《铸造技术》
CAS
2019年第4期376-379,共4页
Foundry Technology
基金
河北省自然科学基金项目(E2015209207)
华北理工大学青年科学研究基金项目(Z201631)
关键词
DP590钢
显微夹杂物
氧氮含量
粒度
DP590 steel
microscopic inclusion
oxygen and nitrogen content
particle size