Ultrafine Ti(C,N)-based cermet was sintered by SPS from 1050℃ to 1450℃ and its sintering properties,such as porosity,mechanical properties and phase transformation,were investigated by optical microscopy (OM),scanning electron microscopy (SEM),X-ray diffraction (XRD),and differential scanning calorimeter (DSC).It is found that the spark plasma sintering properties of Ti(C,N)-based cermet differ from those of conventional vacuum sintering.The liquid phase appearance is at least lower by 150℃ than that in vacuum sintering.The porosity decreases sharply below 1 200℃ and reaches minimum at 1 200℃,and afterwards it almost keeps invariable and no longer increases.SPS remarkably accelerates the phase transformation of Ti(C,N)-based cermet and it has a powerful ability to remove oxides in Ti(C,N)-based cermets.Above 1 350℃,denitrification occurred.Fresh graphite phase formed above 1 430℃.Both the porosity and graphite are responsible for the poor TRS.
Ultrafine Ti(C,N)-based cermet was sintered by SPS from 1050℃ to 1450℃ and its sintering properties,such as porosity,mechanical properties and phase transformation,were investigated by optical microscopy (OM),scanning electron microscopy (SEM),X-ray diffraction (XRD),and differential scanning calorimeter (DSC).It is found that the spark plasma sintering properties of Ti(C,N)-based cermet differ from those of conventional vacuum sintering.The liquid phase appearance is at least lower by 150℃ than that in vacuum sintering.The porosity decreases sharply below 1 200℃ and reaches minimum at 1 200℃,and afterwards it almost keeps invariable and no longer increases.SPS remarkably accelerates the phase transformation of Ti(C,N)-based cermet and it has a powerful ability to remove oxides in Ti(C,N)-based cermets.Above 1 350℃,denitrification occurred.Fresh graphite phase formed above 1 430℃.Both the porosity and graphite are responsible for the poor TRS.
基金
FundedbytheNationalNaturalScienceFoundationofChi na (No .5 0 0 74 0 17)andStateKeyLaboratoryofAdvancedTechnol ogyforMaterialsSynthesisandProcessingofWuhanUniversityofTechnology