电弧离子镀Ni-Co-Cr-Al-Y-Si-B涂层的热腐蚀性能 被引量:4

HOT CORROSION BEHAVIOR OF Ni-Co-Cr-Al-Y-Si-B COATING DEPOSITED BY AIP
下载PDF
导出
摘要 采用电弧离子镀技术在DZ125和DSM11两种镍基高温合金基材上沉积Ni-Co-Cr-Al-Y-Si-B涂层,研究了高温合金基材及其Ni-Co-Cr-Al-Y-Si-B涂层在900℃的75%Na2SO4+25%K2SO4熔盐中的热腐蚀行为.结果表明,Ni-Co-Cr-Al-Y-Si-B涂层在热腐蚀过程中生成了连续致密的α-Al2O3氧化膜,有效地保护了合金基材免受腐蚀破坏,合金基材的热腐蚀性能对体系后期的热腐蚀行为影响很大. Ni-Co-Cr-Al-Y-Si-B coatings were deposited on Ni base superalloys DZ125 and DSM11 by arc ion plating (AIP). The corrosion behaviors of DZ125, DSM11 and Ni-Co-Cr-Al-Y-Si-B coating in molten 75%Na2SO4+25%K2SO4 at 900 ℃ were studied. The results indicate that the coating can protect the DZ125 and DSM11 alloys from hot corrosion destruction due to the formation of a continuous and dense α-Al2O3 scale. In the last stage of the hot corrosion process, the hot corrosion behaviors of base alloys have important influences on behaviors of the whole systems.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 2004年第4期399-403,共5页 Acta Metallurgica Sinica
基金 中国科学院方向性创新课题资助项目KGCX2-212-02
关键词 Ni—Co—CAl—Y—S—B涂层 电弧离子镀 熔盐 热腐蚀 Ni-Co-Cr-Al-Y-Si-B coating, arc ion plating (AIP), molten sulfate, hot corrosion
  • 相关文献

参考文献3

二级参考文献5

  • 1张允书,J Electrochem Soc,1985年,132卷,734页
  • 2Han Y F,Mater Sci Eng A,1997年,239卷,871页
  • 3Li H W,St Erf Coat Technol,1992年,50卷,277页
  • 4马志春译,耐热扩散涂层,1988年,182页
  • 5蔡玉林,高温合金的金相研究,1986年,38页

共引文献11

同被引文献52

引证文献4

二级引证文献18

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部