摘要
通过苯乙烯在氢氧化镁颗粒表面的原位聚合 ,由化学改性法提高了颗粒表面的憎水性和亲油性 ,DSC和熔体流动速率等测定结果表明 :经化学改性提高了氢氧化镁样品的热分解温度 ,使其吸水性明显下降 ,在乙烯 -醋酸乙烯酯共聚物 (EVA)基体树脂中的分散性得到改善 ;SEM观察发现采用原位聚合改性后的氢氧化镁与EVA基体树脂的相容性明显优于未改性氢氧化镁。将其填充EVA ,明显改善了材料的力学性能和加工性能 ,材料的断裂伸长率提高 4倍以上。
The surface of magnesium hydroxide particles was modified via the in-situ polymerization of styrene.Such surface modification increased not only its thermal decomposition temperature,but also the hydrophobicity,as a result,it can readily be dispersed in EVA resins.The mechanical properties of EVA filled with surface modified magnesium hydroxide were greatly improved,with the elongation at break being increased by a factor of four.