Research on the Surface Modification of Pure Zirconium by Electron Beam

Research on the Surface Modification of Pure Zirconium by Electron Beam
下载PDF
导出
摘要 In this paper, the changes of surface morphology, microstructure, hardness and corrosion resistance of industrial pure zirconium before and after surface modification by high current pulsed electron beam were discussed. The microstructure evolution and surface morphologies of the samples were characterized by using X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy (SEM). The experimental results show that sample by high current pulsed electron beam treatment surface melting, martensitic phase transformation occurred, and volcanic crater morphology and fine microstructure in the remelted layer surface;with the increase of number of pulses, after processing the microhardness of the samples also with the increase, 15-pulsed sample microhardness than the original sample increased by 30.9%. Corrosion resistance of samples was studied with the impedance diagram and polarization curve. The electrochemical results show that corrosion resistance of samples by high current pulsed electron beam treatment presents different degrees of change, the 5-pulsed sample in 1 mol HNO<sub>3</sub> solution corrosion of the best, and 15-pulsed sample corrosion resistance is even lower than the original sample. Grain refinement, martensite transformation, dislocation and deformation twins are the main reasons for improving the micro hardness and corrosion resistance of the samples. In this paper, the changes of surface morphology, microstructure, hardness and corrosion resistance of industrial pure zirconium before and after surface modification by high current pulsed electron beam were discussed. The microstructure evolution and surface morphologies of the samples were characterized by using X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy (SEM). The experimental results show that sample by high current pulsed electron beam treatment surface melting, martensitic phase transformation occurred, and volcanic crater morphology and fine microstructure in the remelted layer surface;with the increase of number of pulses, after processing the microhardness of the samples also with the increase, 15-pulsed sample microhardness than the original sample increased by 30.9%. Corrosion resistance of samples was studied with the impedance diagram and polarization curve. The electrochemical results show that corrosion resistance of samples by high current pulsed electron beam treatment presents different degrees of change, the 5-pulsed sample in 1 mol HNO<sub>3</sub> solution corrosion of the best, and 15-pulsed sample corrosion resistance is even lower than the original sample. Grain refinement, martensite transformation, dislocation and deformation twins are the main reasons for improving the micro hardness and corrosion resistance of the samples.
作者 Jinxin Ma Kemin Zhang Xiaolin Zhang Yu Wang Jinxin Ma;Kemin Zhang;Xiaolin Zhang;Yu Wang(College of Materials Engineering, Shanghai University of Engineering Science, Shanghai, China)
出处 《Journal of Materials Science and Chemical Engineering》 2016年第12期46-57,共12页 材料科学与化学工程(英文)
关键词 Pure Zirconium Pulsed Electron Beam Surface Modification Pure Zirconium Pulsed Electron Beam Surface Modification
  • 相关文献

参考文献1

二级参考文献25

  • 1Leyens C, Peters M. Titanium and Titanium Alloys Funda- mentals andApplications[M]. WILEY-VCH Verlag: GmbH & Co. KGaA, 2003:305.
  • 2Gordin D M, Gloriant T, Bohn Met al. Surface and Interface Analysis[J], 2005, 37:1161.
  • 3Li Li, Zhu Youli. Rare Metal Materials and Engineering[J], 2010, 3910: 1754 in Chinese.
  • 4Zhang Yan, Tang Huiping, Li Zengfeng et al. Rare Metal Ma- terials andEngineering[J], 2010, 39S1: 476 in Chinese.
  • 5Chen C H, Ren R M. Rare Metal Materials and Engineering [J], 2010, 39S1: 98 in Chinese.
  • 6Tsuji N, Tanaka S, Takasugi T. Materials Science and Engi- neeringA[J], 2008, 488:139.
  • 7Garcia I, Damborenea J J D. Corrosion Science[J], 1998, 40: 1411.
  • 8Baker T. N, Selamat M S. Materials Science and Technol- ogy[J], 2008, 24:189.
  • 9Zhang Yongzhong, Jin Jutao, Huang Can et al. Rare Metal Materials and Engineering[J], 2010, 398: 1403 in Chinese.
  • 10Yildiz F, Yetim A F, Alsaran A et al. Surface and Coating Technology[J], 2008, 202:2471.

共引文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部