The purpose of the paper is to study the effect of gamma irradiation on the temperature dependence of the dielectric constant and dielectric loss (tanδ) of composite materials PE + x vol% (0≤ x ≤ 10). Measurements are carried out with an alternating current at a frequency of 1 kHz using the measuring bridge E-20. Measurements are carried out at temperature range 300 - 450 K, irradiated at doses of 50, 100 and 150 kGy. It is revealed that in all irradiated samples with increasing volumetric filler content increase the dielectric characteristics of composites PE + x vol%. TlGaSe2. Temperature variation of the dielectric parameters, after gamma irradiation are the result of occurring in the electron-ion and polarization at the interface of the matrix polymer with filler of TlGaSe2.
The purpose of the paper is to study the effect of gamma irradiation on the temperature dependence of the dielectric constant and dielectric loss (tanδ) of composite materials PE + x vol% (0≤ x ≤ 10). Measurements are carried out with an alternating current at a frequency of 1 kHz using the measuring bridge E-20. Measurements are carried out at temperature range 300 - 450 K, irradiated at doses of 50, 100 and 150 kGy. It is revealed that in all irradiated samples with increasing volumetric filler content increase the dielectric characteristics of composites PE + x vol%. TlGaSe2. Temperature variation of the dielectric parameters, after gamma irradiation are the result of occurring in the electron-ion and polarization at the interface of the matrix polymer with filler of TlGaSe2.