オ-ray powder diffraction data and crystal structure of RE compound NdCoGe3 were studied by using X-ray powder diffraction and refined by the Rietveld profile fitting method. The compound has the tetragonal BaNiSn3typ...オ-ray powder diffraction data and crystal structure of RE compound NdCoGe3 were studied by using X-ray powder diffraction and refined by the Rietveld profile fitting method. The compound has the tetragonal BaNiSn3type structure, space group I4mm (No.107) a=0.42961(2) nm, c=098147(4) nm, V=0.018114 nm3, Z=2 and Dx=7.717 g·cm-3. The figure of merit FN for the powder data is F30=623 (0.0107, 45). Structure refinement was performed with 110 reflections and led to Rp=11.78% and Rwp=16.56%.展开更多
The magnetocaloric effect in alloys Gd（Al1-xCox）2 with x = 0, 0.05, and 0.10 were investigated using X-ray diffraction （XRD） and magnetization measurements. It was found that three alloys crystallized in a single ...The magnetocaloric effect in alloys Gd（Al1-xCox）2 with x = 0, 0.05, and 0.10 were investigated using X-ray diffraction （XRD） and magnetization measurements. It was found that three alloys crystallized in a single phase with MgCu2-type structure. The lattice parameter and Curie temperature decreased with increasing Co content, whereas the magnetic-entropy change increased. With a magnetic-field change of 2 T, the maximum of the magnetic-entropy change reached 4.6 J·kg^-1·K^-1 near Curie temperature at approximately 95 K in the alloy GdAl1.8Co0.2, which appeared to be an alternative candidate for active magnetic refrigerants working in the temperature range centered at 100 K.展开更多
The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic wi...The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).展开更多
文摘オ-ray powder diffraction data and crystal structure of RE compound NdCoGe3 were studied by using X-ray powder diffraction and refined by the Rietveld profile fitting method. The compound has the tetragonal BaNiSn3type structure, space group I4mm (No.107) a=0.42961(2) nm, c=098147(4) nm, V=0.018114 nm3, Z=2 and Dx=7.717 g·cm-3. The figure of merit FN for the powder data is F30=623 (0.0107, 45). Structure refinement was performed with 110 reflections and led to Rp=11.78% and Rwp=16.56%.
基金Project supported by the National Natural Science Foundation of China (50371058)
文摘The magnetocaloric effect in alloys Gd（Al1-xCox）2 with x = 0, 0.05, and 0.10 were investigated using X-ray diffraction （XRD） and magnetization measurements. It was found that three alloys crystallized in a single phase with MgCu2-type structure. The lattice parameter and Curie temperature decreased with increasing Co content, whereas the magnetic-entropy change increased. With a magnetic-field change of 2 T, the maximum of the magnetic-entropy change reached 4.6 J·kg^-1·K^-1 near Curie temperature at approximately 95 K in the alloy GdAl1.8Co0.2, which appeared to be an alternative candidate for active magnetic refrigerants working in the temperature range centered at 100 K.
文摘The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).