A diamond-like carbon （DLC） film is deposited as an electron injection layer between the polymer light-emitting layer（MEH-PPV） and aluminum （Al） cathode electrode in polymer electroluminescence devices （PLEDs）...A diamond-like carbon （DLC） film is deposited as an electron injection layer between the polymer light-emitting layer（MEH-PPV） and aluminum （Al） cathode electrode in polymer electroluminescence devices （PLEDs） using a radio frequency plasma deposition system. The source material of the DLC is n-butylamine. The devices consist of indium tin oxide （ITO）/MEH-PPV/DLC/Al. Electron injection properties are investigated through I-V characteristics,and the mechanism of electron injection enhancement due to a thin DLC layer has been studied. It is found that： （1） a DLC layer thinner than 1.0nm leads to a higher turn-on voltage and decreased electroluminescent （EL） efficiency; （2） a 5.0nm DLC layer significantly enhances the electron injection and results in the lowest turn-on voltage and the highest EL efficiency; （3） DLC layer that exceeds 5.0nm results in poor device performance;and（4） EL emission can hardly be detected when the layer exceeds 10.0nm. The properties of ITO/MEH-PPV/DLC/Al and ITO/MEH-PPV/LiF/Al are investigated comparatively.展开更多
By using n-butylamine as carbon resource, diamond-like carbon film (DLCF) was deposited on the p-n porous silicon (PS) surface by means of a radio-frequency glow discharge plasma system. Electroluminescent (EL) spectr...By using n-butylamine as carbon resource, diamond-like carbon film (DLCF) was deposited on the p-n porous silicon (PS) surface by means of a radio-frequency glow discharge plasma system. Electroluminescent (EL) spectra show that EL intensity of the passivated PS diodes increases by 4.5 times and 30-nm blue-shift of EL peak occurs compared with the diodes without treatment and both of them are stable while the passivated diodes are exposed to the air indoor. The current-voltage (I-V) characteristics exhibit that the passivated diodes have a smaller series resistance and a lower onset voltage. The EL intensity-voltage (IEL-V) relations of the PS devices with different DLCF thicknesses show that only medium DLCF thickness is optimum. These experimental phenomena have been explained based on Raman spectra and IR spectra of the diamond-like carbon films and IR spectra of the passivated PS samples.展开更多
文摘A diamond-like carbon （DLC） film is deposited as an electron injection layer between the polymer light-emitting layer（MEH-PPV） and aluminum （Al） cathode electrode in polymer electroluminescence devices （PLEDs） using a radio frequency plasma deposition system. The source material of the DLC is n-butylamine. The devices consist of indium tin oxide （ITO）/MEH-PPV/DLC/Al. Electron injection properties are investigated through I-V characteristics,and the mechanism of electron injection enhancement due to a thin DLC layer has been studied. It is found that： （1） a DLC layer thinner than 1.0nm leads to a higher turn-on voltage and decreased electroluminescent （EL） efficiency; （2） a 5.0nm DLC layer significantly enhances the electron injection and results in the lowest turn-on voltage and the highest EL efficiency; （3） DLC layer that exceeds 5.0nm results in poor device performance;and（4） EL emission can hardly be detected when the layer exceeds 10.0nm. The properties of ITO/MEH-PPV/DLC/Al and ITO/MEH-PPV/LiF/Al are investigated comparatively.
文摘By using n-butylamine as carbon resource, diamond-like carbon film (DLCF) was deposited on the p-n porous silicon (PS) surface by means of a radio-frequency glow discharge plasma system. Electroluminescent (EL) spectra show that EL intensity of the passivated PS diodes increases by 4.5 times and 30-nm blue-shift of EL peak occurs compared with the diodes without treatment and both of them are stable while the passivated diodes are exposed to the air indoor. The current-voltage (I-V) characteristics exhibit that the passivated diodes have a smaller series resistance and a lower onset voltage. The EL intensity-voltage (IEL-V) relations of the PS devices with different DLCF thicknesses show that only medium DLCF thickness is optimum. These experimental phenomena have been explained based on Raman spectra and IR spectra of the diamond-like carbon films and IR spectra of the passivated PS samples.
