It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent densit...It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent density Jis to eliminate the weak link and to control crystallographic anisotropy.It is necessary tomake YBaCuO superconducting bulk have a strong texture with C-axis orientation.Since Jin et al.has suc-展开更多
In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase ...In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase analysis for the sample treated in vacuum condition were made.The results showed that the temperature of phase transition is related to oxygen content in the sample and in general,is 100℃ to 120℃ lower in vacu- um condition than in air.At 320℃ to 350℃ twin bands begin to disappear,and some Cu_2O are formed on the surface of the sample and transit from orthorhombic YBa_2Cu_3O_(7-x) to arthorhombic Y_2BaCuO_5 compound. This transition was completed at about 500℃.Above 900℃,this compound consists of the Y_2BaCuO_5, BaCuO_2,Y_2O_3 and some other minor compounds.No phase transition was observed during cooling the sample.展开更多
文摘It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent density Jis to eliminate the weak link and to control crystallographic anisotropy.It is necessary tomake YBaCuO superconducting bulk have a strong texture with C-axis orientation.Since Jin et al.has suc-
文摘In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase analysis for the sample treated in vacuum condition were made.The results showed that the temperature of phase transition is related to oxygen content in the sample and in general,is 100℃ to 120℃ lower in vacu- um condition than in air.At 320℃ to 350℃ twin bands begin to disappear,and some Cu_2O are formed on the surface of the sample and transit from orthorhombic YBa_2Cu_3O_(7-x) to arthorhombic Y_2BaCuO_5 compound. This transition was completed at about 500℃.Above 900℃,this compound consists of the Y_2BaCuO_5, BaCuO_2,Y_2O_3 and some other minor compounds.No phase transition was observed during cooling the sample.