During the process of liquid forging, a host of hot cracking defects were found in the Al-CuMg-Zn aluminum alloy. Therefore, mechanical tests and analyses by optical microscope, scanning electron microscope, and X-ray...During the process of liquid forging, a host of hot cracking defects were found in the Al-CuMg-Zn aluminum alloy. Therefore, mechanical tests and analyses by optical microscope, scanning electron microscope, and X-ray diffraction were performed to research the influences of zinc, magnesium, and copper(three main alloying elements) on hot cracking tendency and mechanical properties. It was concluded that all the three alloying elements exerted different effects on the performances of newly designed alloys. And the impact of microstructures on properties of alloys was stronger than that of solution strengthening. Among new alloys, Al-5 Cu-4.5 Mg-2.5 Zn alloy shows better properties as follows: σb=327 MPa, δ=2.7%, HB=107 N/mm^2, and HCS=40.展开更多
基金Funded by the International Cooperation Project of the Ministry of Science and Technology of China(No.2014DFR50320)the National Natural Science Foundation of China(No.51174064).
文摘During the process of liquid forging, a host of hot cracking defects were found in the Al-CuMg-Zn aluminum alloy. Therefore, mechanical tests and analyses by optical microscope, scanning electron microscope, and X-ray diffraction were performed to research the influences of zinc, magnesium, and copper(three main alloying elements) on hot cracking tendency and mechanical properties. It was concluded that all the three alloying elements exerted different effects on the performances of newly designed alloys. And the impact of microstructures on properties of alloys was stronger than that of solution strengthening. Among new alloys, Al-5 Cu-4.5 Mg-2.5 Zn alloy shows better properties as follows: σb=327 MPa, δ=2.7%, HB=107 N/mm^2, and HCS=40.