Vibration tests were carried out on three types of stiffened aluminum plates with fully clamped boundaries under random base excitation. During the test, the response of the specimens was monitored using strain gauges...Vibration tests were carried out on three types of stiffened aluminum plates with fully clamped boundaries under random base excitation. During the test, the response of the specimens was monitored using strain gauges. Based on the strain history, the accumulation of fatigue damage of the stiffened plates was estimated by means of the rainflow cycle counting technique and the Miner linear damage accumulation model in the time domain. Utilizing the change of natural frequencies, a nonlinear model was fitted for predicting the fatigue damage of plate and then the foregone failure criterion of 5% reduction in natural frequency is improved. The influence of section and spacing of the stiffeners on the vibration fatigue behavior of the aluminum plate was investigated. The results show that the fatigue life of aluminum plate increases with adding either T or L section riveted stiffeners. With the same cross-sectional area of stiffener, the T section stiffened plate shows longer fatigue life than L section stiffened plate. Meanwhile, the vibration fatigue life also shows great sensitivity to the spacing between the stiffeners.展开更多
To increase the detectability of split Hopkinson pressure bar （SHPB） of low-impedance materials, modifications were conducted on traditional SHPB apparatus with a PMMA tube to output transmitted signal, and weak sig...To increase the detectability of split Hopkinson pressure bar （SHPB） of low-impedance materials, modifications were conducted on traditional SHPB apparatus with a PMMA tube to output transmitted signal, and weak signals were further amplified by semiconductor strain gauges. Experiments on soft rubbers and cushioning foam materials were carried out. In order to analyze the accuracy of the experimental results, the stress equilibrium issues involved in the assumptions of SHPB were investigated. First, by way of re-constructing loading process of incident wave, the stress- strain curve was obtained, along with the stress equilibrium ratio of specimen. Secondly, the influences on the accuracy of stress-strain curves were investigated through the elastic modulus comparisons. And the results illustrate that the bilinear incident wave from experiments can ensure the stress equilibrium deformation of specimen after 2 normalized times, much sooner than ramp incident waves. Moreover, it even facilitates specimen deformation with a constant strain rate. The results confirm that the detectability of the modified SHPB can be down to tens kPa with enough accuracy level.展开更多
基金Project(10932008)supported by the National Natural Science Foundation of ChinaProject(B07050)supported by the Program of Introducing Talents of Discipline to Universities(111 Project),ChinaProject(2012GY2-26)supported by the Key Industry Program of Shaanxi Province,China
文摘Vibration tests were carried out on three types of stiffened aluminum plates with fully clamped boundaries under random base excitation. During the test, the response of the specimens was monitored using strain gauges. Based on the strain history, the accumulation of fatigue damage of the stiffened plates was estimated by means of the rainflow cycle counting technique and the Miner linear damage accumulation model in the time domain. Utilizing the change of natural frequencies, a nonlinear model was fitted for predicting the fatigue damage of plate and then the foregone failure criterion of 5% reduction in natural frequency is improved. The influence of section and spacing of the stiffeners on the vibration fatigue behavior of the aluminum plate was investigated. The results show that the fatigue life of aluminum plate increases with adding either T or L section riveted stiffeners. With the same cross-sectional area of stiffener, the T section stiffened plate shows longer fatigue life than L section stiffened plate. Meanwhile, the vibration fatigue life also shows great sensitivity to the spacing between the stiffeners.
基金Supported by the National Natural Science Foundation(11272267,11102168,10932008)111 Project(B07050)
文摘To increase the detectability of split Hopkinson pressure bar （SHPB） of low-impedance materials, modifications were conducted on traditional SHPB apparatus with a PMMA tube to output transmitted signal, and weak signals were further amplified by semiconductor strain gauges. Experiments on soft rubbers and cushioning foam materials were carried out. In order to analyze the accuracy of the experimental results, the stress equilibrium issues involved in the assumptions of SHPB were investigated. First, by way of re-constructing loading process of incident wave, the stress- strain curve was obtained, along with the stress equilibrium ratio of specimen. Secondly, the influences on the accuracy of stress-strain curves were investigated through the elastic modulus comparisons. And the results illustrate that the bilinear incident wave from experiments can ensure the stress equilibrium deformation of specimen after 2 normalized times, much sooner than ramp incident waves. Moreover, it even facilitates specimen deformation with a constant strain rate. The results confirm that the detectability of the modified SHPB can be down to tens kPa with enough accuracy level.